基于陷阱特性的运行复合绝缘子老化定量评估

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (32133 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract The application of thermal stimulated current (TSC) technique in quantitative- evaluating the serious aging condition of composite insulators has been researched. The composite insulators with different operating years from two manufacturers were used as test samples. The trap characteristics of samples were obtained via TSC technique and the relationship with were studied through SEM and FTIR testing. Experimental results show that, with the increase of operating life, the relative variation ratio of trap charges bears negative relevance with the linear correlation of curve. The trap charges will change obviously only if the aging is more serious, but the aging is not simply aggravated as the operating life increases. The main reasons to form more trap charges lie in that the new physical states and chemical structures are produced during the aging process of composite insulators. The thresholds of trap charge variation ratio for the two manufactures were confirmed respectively, indicating the serious aging of composite insulators.

Key words： Composite insulators aging quantitative evaluation thermal stimulated current volume-resistivity and temperature

Received: 25 August 2014 Published: 20 October 2015

PACS:

TM835

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	Liang Ying
	Jin Zhe
	Liu Yunpeng
	Chen Yixin

Cite this article:

Liang Ying,Jin Zhe,Liu Yunpeng等. The Quantitative-Evaluation on the Aging Condition of Composite Insulators Based on Trap Characteristics[J]. Transactions of China Electrotechnical Society, 2015, 30(18): 189-185.

URL:

https://dgjsxb.ces-transaction.com/EN/ OR https://dgjsxb.ces-transaction.com/EN/Y2015/V30/I18/189

[1] 关志成. 绝缘子及输变电设备外绝缘[M]. 北京: 清华大学出版社, 2006.
[2] 程养春, 李成榕, 王晓刚, 等. DL-1型合成绝缘子检测仪现场测试分析[J]. 高电压技术, 2003, 29(5): 42-44. Cheng Yangchun, Li Chengrong, Wang Xiaogang, et al. Analysis of Field Test of DL-1 composite insulator detector[J]. High Voltage Engineering, 2003, 29(5): 42-44.
[3] Berg M, Thottappillil R, Scuka V, et al. Hydrophobi-
city estimation of HV polymeric insulating materials development of a digital image processing method[J]. IEEE Transactions on and Electrical Insulation Society, 2001, 8(6): 1098-1107.
[4] 唐良瑞, 张晶, 孙毅. 基于信息测度和Hausdorff 距离的复合绝缘子憎水性等级判定[J]. 电工技术学报, 2009, 24(1): 35-41. Tang Liangrui, Zhang Jing, Sun Yi, et al. Estimating the level of hydrophobicity of composite insulators based on information measures and hausdorff distance[J]. Transactions of China Electrotechnical Society, 2009, 24(1): 35-41.
[5] 徐征, 郭盼, 何晓龙, 等. 基于核磁共振原理的复合绝缘子老化问题研究[J]. 高压电器, 2012,48(3): 21-25. Xu Zheng, Guo Pan, He Xiaolong, et al. Aging detection of composite insulator with nuclear magnetic resonance theory[J]. High Voltage Apparatus, 2012, 48(3): 21-25.
[6] 尹毅, 肖登明, 屠德民, 等. 空间电荷在评估绝缘聚合物电老化程度中的应用研究[J]. 中国电机工程学报, 2002, 22(1): 43-48. Yin Yi, Xiao Dengming, Tu Demin. An application of space charge in valuing the electric ageing degree of insulating polymer[J]. Proceedings of the CSEE, 2002, 22(1): 43-48.
[7] Moudoud M, Megherbi M, Mekious M, et al. Thermal aging effect on charging and discharging currents in polymers under DC stress[C]. IEEE International Symposium on Electrical Insulation, 2008: 506-509.
[8] Mazzanti G, Montanari G C, Palmieri F. Quantities extracted from space-charge measurements as markers for insulation aging[J]. IEEE Transactions on Dielectrics and Electrical Insulation, 2003, 10(2): 198-203.
[9] Chen G, Fu M, Liu X Z, et al. AC aging and space-charge characteristics in low-density polyethylene polymeric insulation[J]. Journal of Applied Physics, 2005, 97(8): 1-7.
[10] 尹毅, 肖登明, 屠德民, 等. TSC/TSL联合谱在绝缘聚合物电老化研究中的应用[J]. 中国电机工程学报, 2002, 22(3): 1-5. Yin Yi, Xiao Dengming, Tu Demin, et al. Application of TSC/TSL-united-spectra in investigation of electrical aging in insulating polymer[J]. Proceedings of the CSEE, 2002, 22(3): 1-5.
[11] 梁英, 李成榕, 丁立健, 等. 合成绝缘子材料TSC试验研究[J]. 电工技术学报, 2006, 21(2): 13-16, 26. Liang Ying, Li Chengrong, Ding Lijian, et al. Experimental test on TSC of the composite insulators[J]. Transactions of China Electrotechnical Society, 2006, 21(2): 13-16, 26.
[12] 张辉, 屠幼萍, 佟宇梁, 等. 基于TSC测试的硅橡胶复合绝缘子伞裙材料老化特性研究[J]. 中国电机工程学报, 2012, 32(19): 169-174. Zhang Hui,Tu Youping, Tong Yuliang, et al. Study on aging characteristics of Silicone rubber sheds of composite insulators based on TSC test[J]. Proceedings of the CSEE, 2012,32(19):169-174.
[13] 梁英. 高温硫化（HTV）硅橡胶电晕老化特性及机理的研究[D]. 保定: 华北电力大学, 2008.
[14] 李长明. 高分子绝缘材料化学基础[M]. 哈尔滨: 哈尔滨工业大学出版社, 2007.
[15] 吴其晔, 张萍, 杨文君, 等. 高分子物理学[M]. 北京: 高等教育出版社, 2011.
[16] 杨晓辉. 基于傅立叶变换红外光谱测试的复合绝缘子老化评估方法研究[D]. 保定: 华北电力大学, 2012.
[17] 李聪. 复合绝缘子热刺激电流测量的实现与应用[D]. 保定: 华北电力大学, 2012.
[18] 陈逸昕. 人工电晕老化条件下复合绝缘子材料体积电阻率特性研究[D]. 保定: 华北电力大学, 2013.
[19] Liao K, Chen H, Awad S, et al. Determination of free-volume properties in polymers without orthopo-
sitronium components in positron annihilation lifetime spectroscopy[J]. Macromolecules, 2011, 44(17): 6818-
20 6826.
[20] Bin Ma, Johan Andersson, Stanislaw M Gubanski. Evaluating resistance of polymeric materials for outdoor applications to corona and ozone[J]. IEEE Transactions on Dielectrics and Electrical Insulation, 2010, 17(2): 555-565.
[21] Bin Ma, Stanislaw M Gubanski. AC and DC Corona/Ozone-induced ageing of HTV Silicone rubber[J]. IEEE Transactions on Dielectrics and Electrical Insulation, 2011, 18(6): 1984-1994.
[22] 王建国, 刘洋, 方春华, 等. 交流电流对高温硫化硅橡胶性能的影响[J]. 高分子学报, 2009(4): 331- 337. Wang Jianguo, Liu Yang, Fang Chunhua, et al. Performance influence of high temperature vulcanization silicone rubber by alternating current corona discharge[J]. Acta Polymerica Sinica, 2009(4): 331-337.
[23] 梁曦东, 李震宇, 周远翔. 交流电晕对硅橡胶材料憎水性的影响[J]. 中国电机工程学报, 2007, 27(27) : 19-23. Ling Xidong, Li Zhenyu, Zhou Yuanxiang. Influences of AC corona on hydrophobicity of silicone rubber [J]. Proceedings of the CSEE, 2007, 27(27): 19-23