硫化压力对500 kV超高压直流XLPE电缆工厂接头恢复绝缘性能的影响

doi:10.19595/j.cnki.1000-6753.tces.240760

Abstract
Figure/Table
References (0)
Related Citation (15)

Download: PDF (1019 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract

The increasing distance of offshore wind farms from coastal areas has created an urgent need for the development of long-term extra high voltage direct current (EHVDC) cables. Factory joints are commonly used to connect sections of submarine cables, forming extensive cable systems. Therefore, studying factory joint is crucial for advancing long-length cable lines. This study investigates the physicochemical and dielectric insulation characteristics of XLPE samples under various vulcanization pressures, highlighting the effects of these pressure changes on the properties of 500 kV EHVDC cross-linked polyethylene (XLPE) cable joints.
Commercially available 500 kV EHVDC XLPE pellets were used to prepare the XLPE samples via hot-press method. Initially, a specified quantity of XLPE pellets was distributed between two iron plates. The pellets were preheated at 120℃ for 5 minutes and then heated at 180℃. Cross-linking was subsequently performed under different vulcanization pressures of 1.3 MPa, 1.6 MPa, 1.9 MPa and 2.5 MPa respectively. The fabricated XLPE specimens underwent physical characterization through Fourier-transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), X-ray diffraction (XRD), and gel content analysis. While electrical measurements included current density analysis, pulsed electro-acoustic (PEA) analysis, and DC breakdown test.
The physiochemical results indicate that increasing vulcanization pressure enhances the crosslinking degree of XLPE samples, transforming the material from a linear molecular structure to a 3D network structure and breaking macromolecules into smaller, mobile molecules. The increased mobility of these small molecules leads to improved crystallinity, resulting in a higher crystallinity structure. Additionally, the recrystallized macromolecular chains have higher melting temperatures, raising the overall melting temperature of the samples. However, higher vulcanization pressure also produces crosslinking by-products that are difficult to decompose and volatilize. The combination of high temperatures and pressures causes thermal expansion forces perpendicular to the lamellae, increasing lamella spacing, creating more amorphous regions, and effecting the insulation performance of the samples.
Regarding electric insulation performance, the DC breakdown strength and space charge injection threshold strength of the fabricated XLPE samples initially increase and then decrease with the increase in vulcanization pressure. Conversely, conductivity current and average space charge density first decrease and then increase. An optimal vulcanization pressure of 1.9 MPa was identified, at which the XLPE samples exhibited improved electrical insulation properties. Below this pressure, the increased trap energy levels inhibit carrier transport, thereby reducing the number of free carrier paths and hindering the formation of conductive channels, ultimately increasing the breakdown strength of the XLPE samples. However, at vulcanization pressures above 1.9 MPa, the increased crosslinking byproducts create more shallow traps, which lower space charge injection and accumulation, ultimately distorting the sample's internal electric field. Additionally, the increased lamella spacing creates more amorphous regions, reducing the carrier transport barrier and further decrease the breakdown strength of the prepared XLPE samples.
Based on the results, it can be concluded that appropriately increasing the vulcanization pressure of factory joints improves the physicochemical and electrical properties of XLPE. However, excessively high vulcanization pressure can have a detrimental impact on the electrical insulation properties of cable factory joints.

Key words： Vulcanization pressure cross-linked polyethylene extra high voltage direct current cable factory joints return insulation

Received: 12 May 2024

PACS:

TM85

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	Zhang Tianyin
	Chen Xiangrong
	Wang Enzhe
	Yin Kai
	Xia Feng
	Huang Ruobin

Cite this article:

Zhang Tianyin,Chen Xiangrong,Wang Enzhe等. Effect of Vulcanization Pressure on the Return Insulation Performance of 500 kV EHVDC XLPE Cable Factory Joints[J]. Transactions of China Electrotechnical Society, 0, (): 2492942-2492942.

URL:

https://dgjsxb.ces-transaction.com/EN/10.19595/j.cnki.1000-6753.tces.240760 OR https://dgjsxb.ces-transaction.com/EN/Y0/V/I/2492942

[1] 杜伯学, 韩晨磊, 李进, 等. 高压直流电缆聚乙烯绝缘材料研究现状[J]. 电工技术学报, 2019, 34(1): 179-191.
Du Boxue, Han Chenlei, Li Jin, et al.Research status of polyethylene insulation for high voltage direct current cables[J]. Transactions of China Electrotechnical Society, 2019, 34(1): 179-191.
[2] 刘耀, 赵小令, 吴佳玮, 等. 高压直流海缆工程应用现状及展望[J]. 高压电器, 2022, 58(2): 1-8.
Liu Yao, Zhao Xiaoling, Wu Jiawei, et al.Application status and prospect of HVDC submarine cable projects[J]. High Voltage Apparatus, 2022, 58(2): 1-8.
[3] 朱敏慧, 闵道敏, 高梓巍, 等. 直流电缆用交联聚乙烯绝缘的击穿概率及其尺度效应仿真[J]. 电工技术学报, 2024, 39(4): 1172-1184.
Zhu Minhui, Min Daomin, Gao Ziwei, et al.Breakdown probability and size effect simulation of XLPE insulation for DC power cables[J]. Transactions of China Electrotechnical Society, 2024, 39(4): 1172-1184.
[4] 钟力生, 任海洋, 曹亮, 等. 挤包绝缘高压直流电缆的发展[J]. 高电压技术, 2017, 43(11): 3473-3489.
Zhong Lisheng, Ren Haiyang, Cao Liang, et al.Development of high voltage direct current extruded cables[J]. High Voltage Engineering, 2017, 43(11): 3473-3489.
[5] Mazzanti G, Castellon J, Chen G, et al.The insulation of HVDC extruded cable system joints. Part 1: Review of materials, design and testing procedures[J]. IEEE Transactions on Dielectrics and Electrical Insulation, 2019, 26(3): 964-972.
[6] Saltzer M, Gustafsson A, Jeroense M, et al.A new voltage level for extruded DC cables[C]//CIGRE Session 2016, Paris, France, 2016: B1-301.
[7] 赵薇, 张振鹏, 胡列翔, 等. 500 kV海缆接头绝缘恢复对XLPE工频击穿和晶相结构的影响[J]. 高电压技术, 2019, 45(11): 3437-3444.
Zhao Wei, Zhang Zhenpeng, Hu Liexiang, et al.Effects of 500 kV submarine cable factory joint insulation recovery on power frequency breakdown and crystalline morphology of XLPE[J]. High Voltage Engineering, 2019, 45(11): 3437-3444.
[8] 苏鹏飞, 吴建东, 祝曦, 等. 脱气处理对直流电缆绝缘击穿场强的影响[J]. 中国电机工程学报, 2020, 40(2): 663-672.
Su Pengfei, Wu Jiandong, Zhu Xi, et al.Effect of degassing treatment on breakdown strength in direct current cable insulation[J]. Proceedings of the CSEE, 2020, 40(2): 663-672.
[9] Du Boxue, Zhu Xiaohui, Gu Liang, et al.Effect of surface smoothness on tracking mechanism in XLPE-Si-rubber interfaces[J]. IEEE Transactions on Dielectrics and Electrical Insulation, 2011, 18(1): 176-181.
[10] Doedens E, Jarvid E M, Frohne C, et al.Enhanced charge injection in rough HVDC extruded cable interfaces[J]. IEEE Transactions on Dielectrics and Electrical Insulation, 2019, 26(6): 1911-1918.
[11] 孟繁博, 陈向荣, 洪泽林, 等. 界面喷涂Mg(OH)2对直流电缆工厂接头绝缘交接层直流电气性能的影响[J]. 电工技术学报, 2023, 38(23): 6471-6482.
Meng Fanbo, Chen Xiangrong, Hong Zelin, et al.Influence of interface spraying Mg(OH)2 on DC electrical properties of DC cable factory joints insulation transition layer[J]. Transactions of China Electrotechnical Society, 2023, 38(23): 6471-6482.
[12] 周厚强. 含软接头的220kV光纤复合海底电缆的研制[J]. 电线电缆, 2012(6): 4-7, 40.
Zhou Houqiang.Research and development of the factory joint inside optical fiber composite submarine cable for rated voltage of 220 kV[J]. Electric Wire & Cable, 2012(6): 4-7, 40.
[13] 董芸滋, 高嫄, 李秀峰, 等. 交联度对交联聚乙烯/有机化蒙脱土纳米复合材料拉伸性能和介电性能的影响[J]. 电工技术学报, 2023, 38(5): 1154-1165.
Dong Yunzi, Gao Yuan, Li Xiufeng, et al.Effect of crosslinking degree on tensile and dielectric properties of cross-linked polyethylene/organic montmorillonite nanocomposite material[J]. Transactions of China Electrotechnical Society, 2023, 38(5): 1154-1165.
[14] Wei Yanhui, Yang Jingjing, Li Guochang, et al.Influence of molecular chain side group on the electrical properties of silicone rubber and mechanism analysis[J]. IEEE Transactions on Dielectrics and Electrical Insulation, 2022, 29(4): 1465-1473.
[15] Xu Nuo, Zhong Lisheng, Sui Rui, et al.Correlation between terahertz dielectric properties of XLPE and its composition structure during electrothermal aging[J]. Macromolecules, 2022, 55(18): 8186-8194.
[16] 段玉兵, 韩明明, 王兆琛, 等. 不同热老化温度下高压电缆绝缘特性及失效机理[J]. 电工技术学报, 2024, 39(1): 45-54.
Duan Yubing, Han Mingming, Wang Zhaochen, et al.Insulation characteristics and failure mechanism of high-voltage cables under different thermal aging temperatures[J]. Transactions of China Electrotechnical Society, 2024, 39(1): 45-54.
[17] 陶霰韬, 李化, 方田, 等. 基于片晶滑移的水树结晶破坏机理[J]. 电工技术学报, 2021, 36(12): 2640-2649.
Tao Xiantao, Li Hua, Fang Tian, et al.Crystalline destruction mechanism caused by water tree based on lamella slip[J]. Transactions of China Electrotechnical Society, 2021, 36(12): 2640-2649.
[18] Contat-Rodrigo L, Ribes Greus A.Biodegradation studies of LDPE filled with biodegradable additives: Morphological changes. I[J]. Journal of Applied Polymer Science, 2002, 83(8): 1683-1691.
[19] Jiang H G, Rühle M, Lavernia E J.On the applicability of the X-ray diffraction line profile analysis in extracting grain size and microstrain in nanocrystalline materials[J]. Journal of Materials Research, 1999, 14(2): 549-559.
[20] 雷清泉, 刘关宇. 如何理解工程电介质中极化与电导两个基本物理过程及其测量的科学原理与方法[J]. 中国电机工程学报, 2018, 38(23): 6769-6789, 7113.
Lei Qingquan, Liu Guanyu.How to understand the two basic physical processes of polarization and conductance in engineering dielectrics and scientific principles and methods of their measurement[J]. Proceedings of the CSEE, 2018, 38(23): 6769-6789, 7113.
[21] Akram S, Yang Yan, Zhong Xin, et al.Influence of nano layer structure of polyimide film on space charge behavior and trap levels[J]. IEEE Transactions on Dielectrics and Electrical Insulation, 2018, 25(4): 1461-1469.
[22] Li Guochang, Wang Zhaochen, Lan Rui, et al.The lifetime prediction and insulation failure mechanism of XLPE for high-voltage cable[J]. IEEE Transactions on Dielectrics and Electrical Insulation, 2023, 30(2): 761-768.
[23] Li Jianying, Zhou Fusheng, Min Daomin, et al.The energy distribution of trapped charges in polymers based on isothermal surface potential decay model[J]. IEEE Transactions on Dielectrics and Electrical Insulation, 2015, 22(3): 1723-1732.
[24] 闫群民, 李欢, 翟双, 等. 不同温度热老化对高压配网交联聚乙烯电缆绝缘表面陷阱参数的影响[J]. 中国电机工程学报, 2020, 40(2): 692-701.
Yan Qunmin, Li Huan, Zhai Shuang, et al.Effect of thermal aging at different temperatures on the surface trap parameters of HV-XLPE distribution cable insulation[J]. Proceedings of the CSEE, 2020, 40(2): 692-701.
[25] 朱晓辉, 杜伯学, 高宇, 等. 交联工艺对交联聚乙烯结晶形态的影响[J]. 绝缘材料, 2010, 43(6): 44-47.
Zhu Xiaohui, Du Boxue, Gao Yu, et al.Effects of cross-linking process on crystallinity of XLPE[J]. Insulating Materials, 2010, 43(6): 44-47.