压接式复合绝缘子疲劳破坏的机理分析

Abstract
Figure/Table
References
Related Citation (15)

Download: PDF (1478 KB) HTML (1 KB)
Export: BibTeX | EndNote (RIS)

Abstract In this paper,the crimped composite insulators are studied. For the problems that is the crimped composite insulators are prone to fatigue failure under the alternating loads on overhead lines; Fatigue failure mechanism of the crimped composite insulators are analyzed from three aspects that is the mandrel substrate material, structural crafts and fatigue fracture, respectively. The conclusion is obtained,that is the capacity of composite insulator withstanding tensile load is much better than withstanding pressure load capacity and the cause of generation stress concentration between the metal fittings and the mandrel. The results show that fatigue failure first occurred in the outer surface of the connection zone and expand from the surface to the entrails. That results provided a new ideas for analyzing fracture cause and referencing to design a new type of anti-fatigue structural of the composite insulators.

Key words： Composite insulators fatigue damage mechanism

Received: 22 September 2013 Published: 05 November 2014

PACS:

TM216+.3

	Service

	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	Xie Zhanshan
	Wang Zhangqi
	Chen Yuan
	Lu Yi

Cite this article:

Xie Zhanshan,Wang Zhangqi,Chen Yuan等. Analysis of Damage Mechanism for Crimped Composite Insulators[J]. Transactions of China Electrotechnical Society, 2014, 29(6): 296-302.

URL:

http://dgjsxb.ces-transaction.com/EN/ OR http://dgjsxb.ces-transaction.com/EN/Y2014/V29/I6/296

[1] 范建斌, 殷禹, 张锦秀, 等. 复合绝缘子运行状况评估方法[J]. 电网技术, 2006, 30(12): 24-27. Fan Jianbin, Yin Yu, Zhang Jinxiu, et al. Evaluation methods for operational status of composite insulators [J]. Power System Technology, 2006, 30(12): 24-27.
[2] 刘泽洪. 复合绝缘子使用现状及其在特高压输电线路中的应用前景[J]. 电网技术, 2006, 30(12): 1-7. Liu Zehong. Present situation and prospects of applying composite insulators to UHF transmission lines in China[J]. Power System Technology, 2006, 30(12): 1-7.
[3] 崔江流. 我国硅橡胶合成绝缘子的应用与展望[J].中国电力, 1999, 32(1): 38-41. Cui Jiangliu. The application and its prospect of silicon rubber composite insulators in China[J]. Electric Power, 1999, 32(1): 38-41.
[4] 吴光亚. 提高复合绝缘子长期动行可靠性的措施[J]. 有机硅材料, 2008, 22(3): 176-178. Wu Guangya. Measurements of improvement on reliability of composite insulatorsin long-term operation [J]. Silicone Material, 2008, 22(3): 176-178.
[5] 王丽雪, 尹志娟, 刘海鸥. 玻璃纤维增强环氧树脂单向复合材料力学性能分析[J]. 黑龙江工程学院学报(自然科学版), 2009, 23(3): 73-74. Wang Lixue, Yin Zhijuan, Liu Hai’ou. Study on mechanical properties of unidirectional glass fiber reinforced epoxy resin composites[J]. Journal of Heilongjiang Institute of Technology, 2009, 23(3): 73-74.
[6] 余志宏. 复合绝缘子压接金具弹塑性分析[J]. 电磁避雷器, 2000, 174(2): 9-11. Yu Zhihong. Analysis on elastic and plastic deformation of extruded metal fitting on composite insulators[J]. Insulators and Surge Arresters, 2000, 174(2): 9-11.
[7] 余涛, 杨新华. 压接式复合绝缘子接头处的破坏分析[J]. 水电能源科学, 2010, 28(10): 139-141. Yu Tao, Yang Xinhua. Failure analysis of connector of crimp-style composite insulator[J]. Water Resources and Power, 2010, 28(10): 139-141.
[8] Wankowicz J, Bielecki J. Models of the long-term mechanical strength of long rod composite insulators[C]. IEEE Transactions on Dielectrics and Electrical Insulation, 2010, 17(2): 360-367.
[9] 卢明良. 夹头出口处导线动弯应变与弯曲振幅关系的理论分析[J]. 东北电力技术, 1995(4): 7-10. Lu Mingliang. The theoretical analysis of wire’s dynamic bending strain and bending amplitude relations on the chuck outlet[J]. North Eastern Electric Power, 1995(4): 7-10.
[10] Kumosa M, Han Y, Kumosa L. Analyses of composite insulators with crimped endfittings: part II—Suitable crimping conditions[J]. Coposites Science and Technology, 2002, 62(9): 1209-1221.
[11] 谢占山. 500kV“V”串复合绝缘子机械疲劳试验研究[D]. 保定: 华北电力大学, 2012.